Steel / Foundry

UKCG Magnesium Granules are utilised within the Iron and Steel industry for the desulphurization process. UKCG offer a product line which encompasses pure magnesium granules, magnesium alloys and blends all used in hot metal desulphurization applications. The process of desulphurization ensures optimum corrosion resistance of steel product.

Magnesium is used in foundry application for the modification of laminar graphite inclusions to nodular graphite shape. This ensures better physical properties of the cast iron.

Product Specification

UKMG – MG200/800

UKMG – MG200/800

Application Chemical industry, steel industry
Composition Made from Mg
Min 99,90 %
Granulation Mg powder 200/1000
Typical screen analyses to JEL 200
Screen inlet: DIN 418
> 0,8 mm 5 % max
0.5-0.8 mm 50-80 %
0.2-0.5 mm 10-40 %
< 0.2 mm traces
Apparent Density Approx. 900 kg/m3
Special Properties Due to a special production procedure a low oxide content is achieved
Packaging UN Certified big bags

UKMG-RA90/10 – MG200/800

UKMG-RA90/10 – MG200/800

Application Steel industry, hot metal desulphurization
Composition Made from Mg, min. 99,90 % mixed with 10 % high fluidized lime and Aluminum, stabilized and flow treated
Granulation Mg powder 200/800
Typical screen analyses to JEL 200
Screen inlet: DIN 4188
> 0,8 mm max 5 %
0.5-0.8 mm 50-80 %
0.2-0.5 mm 10-40 %
< 0.2 mm traces
Apparent Density Approx. 850 – 900 kg/m3
Special Properties Due to a special production procedure a low oxide content is achieved
Product is flow treated.
Packaging UN Certified big bags

UKMG-RA90/10 – MGR200/800

UKMG-RA90/10 – MGR200/800

Application Steel industry, hot metal desulphurization
Composition Made from Mg secondary ingots, min 90 % Mg, 9 % Al, 1 % various elements, stabilised and flow treated
Granulation Mg alloy powder 200/800
Typical screen analyses to JEL 200
Screen inlet: DIN 4188
> 0,8 mm 5 % max
0.5-0.8 mm 45-85 %
0.2-0.5 mm 10-50 %
< 0.2 mm traces
Apparent Density Approx. 800 – 900 kg/m3
Special Properties Due to a special production procedure a low oxide content is achieved
Product is flow treated.
Packaging UN Certified big bags

UKMG-RA97/3 – MGR200-1000

UKMG-RA97/3 – MGR200-1000

Application Chemical industry, steel industry
Composition Made from Mg
Min 99,90 %
Granulation Mg powder 200/1000
Typical sieve analyse to JEL 200
Sieve inlet: DIN 4188
> 0,8 mm 5 % max
0.5-0.8 mm 50-80 %
0.2-0.5 mm 10-40 %
< 0.2 mm traces
Apparent Density Approx. 900 kg/m3
Special Properties Due to a special production procedure a low oxide content is achieved.
Product is flow treated.
Packaging UN Certified big bags